Part 298

Lanthanum oxide 30 parts Yttrium oxide 20 parts Burnt magnesia 50 parts Acetic acid 50 parts Water, distilled 100 parts

The salts are dissolved in the water, and to the solution another 150 parts of distilled water are added and the whole filtered. The vegetable fiber (in its knitted or woven form) is impregnated with this solution dried, and arranged on platinum wire. In the formula the acetic acid may be replaced with dilute nitric acid. The latter seems to have some advantages over the former, among which is the fact that the residual ash where acetic acid is used has a tendency to ball up and make a vitreous residue, while that of the nitric acid remains in powdery form.

«Self-Igniting Mantles.»—A fabric of platinum wire and cotton thread is sewed or woven into the tissue of the incandescent body; next it is impregnated with a solution of thorium salts and dried. The thorium nitrate in glowing gives a very loose but nevertheless fireproof residue. A mixture of thorium nitrate with platinic chloride leaves after incandescence a fire-resisting sponge possessing to a great extent the property of igniting gas mixtures containing oxygen. Employ a mixture of 1 part of thorium nitrate to 2 1⁠/⁠2 parts of platinic chloride.

MANURES: See Fertilizers.

MANUSCRIPT COPYING: See Copying.

MAPLE: See Wood.

MARASCHINO: See Wines and Liquors.

MARBLE CEMENTS: See Adhesives.

MARBLE CLEANING: See Cleaning Preparations and Methods.

MARBLE COLORS: See Stone.

MARBLE ETCHING: See Etching.

MARBLE, IMITATION: See Plaster.

MARBLE, PAINTING ON: See Painting.

MARBLE POLISHING: See Polishes.

MARBLING CRAYONS: See Crayons.

MARGERINE: See Butter.

«MARKING FLUID:»

See also Inks and Etching.

For laying out work on structural iron or castings a better way than chalking the surface is to mix whiting with benzine or gasoline to the consistency of paint, and then apply it with a brush; in a few minutes the benzine or gasoline will evaporate, leaving a white surface ready for scribing lines.

MASSAGE APPLICATIONS: See Cosmetics.

MASSAGE SOAPS: See Soaps.

«Matches»

(See also Phosphorus.)

«Manufacture of Matches.»—Each factory uses its own methods and chemical mixtures, though, in a general way the latter do not vary greatly. It is {466} impossible here to give a full account of the different steps of manufacture, and of all the precautions necessary to turn out good, marketable matches. In the manufacture of the ordinary safety match, the wood is first comminuted and reduced to the final shape and then steeped in a solution of ammonium phosphate (2 per cent of this salt with 1 or 1 1⁠/⁠2 per cent of phosphoric acid), or in a solution of ammonium sulphate (2 1⁠/⁠2 per cent), then drained and dried. The object of this application is to prevent the match from continuing to glow after it has been burned out. Next the matches are dipped into a paraffine or stearine bath, and after that into the match bath proper, which is best done by machines constructed for the purpose. Here are a few formulas:

I.—Potassium chlorate 2,000 parts Lead binoxide 1,150 parts Red lead 2,500 parts Antimony trisulphide 1,250 parts Gum arabic 670 parts Paraffine 250 parts Potassium bichromate 1,318 parts

Directions: See No. II.

II.—Potassium chlorate 2,000 parts Lead binoxide 2,150 parts Red lead 2,500 parts Antimony trisulphide 1,250 parts Gum arabic 670 parts Paraffine 250 parts

Rub the paraffine and antimony trisulphide together, and then add the other ingredients. Enough water is added to bring the mass to a proper consistency when heated. Conduct heating operations on a water bath. The sticks are first dipped in a solution of paraffine in benzine and then are dried. For striking surfaces, mix red phosphorus, 9 parts; pulverized iron pyrites, 7 parts; pulverized glass, 3 parts; and gum arabic or glue, 1 part, with water, quantity sufficient. To make the matches water or damp proof, employ glue instead of gum arable in the above formula, and conduct the operations in a darkened room. For parlor matches dry the splints and immerse the ends in melted stearine. Then dip in the following mixture and dry: